淀粉浆液的黏附力研究-《现代纺织技术》(2019年2期).docx

龙源版权所有 淀粉浆液的黏附力研究作者：李媛 钱现来源：《现代纺织技术》2019年第02期 摘要：为研究淀粉在低温时的上浆效果，采用粗纱试验法对玉米淀粉、氧化淀粉、SPR淀粉和A115淀粉浆液在不同温度下（90、70、50℃）的黏附力进行测试。结果表明，4种淀粉对粗纱的黏附力随温度的升高而增大;玉米淀粉的黏附力最大，SPR淀粉和A115淀粉在低温时的黏附力好，适宜低温上浆。上述结论可为低温上浆的可行性提供重要参考。 关键词：淀粉浆料;粗纱试验法;低温上浆;黏附力 中图分类号：TS105.2 文献标志码：A 文章编号：1009-265X（2019）02-0018-03 Abstract：to study the sizing effect of starch at a low temperature， roving experiment method was applied to test adhesive force of corn starch， oxidized starch， SPR starch and A115 starch slurry under different temperatures （90 ℃， 70 ℃ and 50 ℃）. The results showed that， adhesive force of the 4 kinds of starch to roving increased with temperature rise. Corn starch presented the maximum adhesive force. SPR starch and A115 starch showed good adhesive force at the low temperature， and they were suitable for low-temperature sizing. The above conclusion can provide important reference for the feasibility of low-temperature sizing. Key words：starch slurry; roving experiment method; low-temperature sizing; adhesive force 淀粉是一种来源广泛的可再生的天然高聚物化合物，其特征在于容易被生物降解，环境污染小，价格低等，因而其一向都是浆纱工艺中重要的黏着剂[1]。浆料的选用在浆纱工艺中有着非常重要的作用，一般通过浆料的成膜性及黏附性来评价浆料性能的好坏，判断其能否适用于漿纱。黏附性通常用黏附力的大小来反映。影响黏附力大小的因素有纤维与浆料之间的黏附性能及浆料自身的内聚力，两个聚合物之间的黏附以化学黏附、热力学黏附和机械黏附3种形式存在。而在浆纱中，浆料对纤维的有效黏附以热力学黏附和机械黏附为主，在后整理过程中必须把浆料从织物中除去，因而浆料与纤维之间不能有化学键结合，又称不允许有化学黏附[2]。黏附力作为浆液的质量指标之一，结合了浆膜自身的强度和浆液对纱线以及织物的黏附力两个方面之间的性能，直接反映了经纱上浆后的可织造性能。通常淀粉对棉纤维、麻纤维、黏胶等纤维素纤维有很好的黏附性[3]。 浆液的黏附力测试主要有粗纱法及织物条试验法两种方法[4]。一般采用较多的是粗纱试验法，这是由于粗纱自身的强力很小，在试验时粗纱自身的强力大小可忽略不计，因而可用浆纱后粗纱的断裂强力的大小来反应浆液的黏附力。这种方法相对比较简单，可以适用于纺织企业对浆料性能的简单评价，而且与上浆实践中采用的细纱情况相近，···试读结束