工 艺技术 工 艺技术 2014年10月 涂料工业 PAINT COATINGS [NDUSTRY Vol. 44 No.10 Oct 2014 含半结晶聚酯的TGIC型粉末涂料的耐老化性能研究 李 勇12,瞿金清,顾宇昕2,刘亮2,何涛2 (1. 华南理工大学广州510640;2. 中国电器科学研究院有限公司广州510641) 摘要：合成了半结晶型聚酯树脂和无定形聚酯树脂，并以其分别制备了粉末涂料。通过人工加 速老化、衰减全反射红外和扫描电镜表征了半结晶和无定形2类聚酯粉末涂层的耐老化性能，发现半 结晶聚酯粉末涂料的耐老化性能不如无定形聚酯粉末涂料。 关键词：半结晶聚酯树脂； 粉末涂料； 耐候性能 中图分类号：TQ637.82 文献标识码：A 文章编号：0253-4312(2014)10-0033-05 Study on Anti- Aging Properties of TGIC-Curing Powder Coatings Comprising Semi — Crystal Polyester Resins Li Yong12,QuJinqin12,Gu Yuxin12,Liu Liang2,HeTao12 (1 South China University of Technology,Guangzhou 510640,China;2 China National Electric Apparatus Research Institute Co ,Lld,Guangzhou 510641,China) Abstract:The semi - crystal and amorphous polyester resins were synthesized ,which were further used respectively to prepare TGIC- curing powder coatings. The anti-aging property of the said powder coatings was characterized by the artificial accelerated aging tester,ATR- FTIR and SEM It was found that the anti-aging property of semi-crystal polyester powder coatings was inferior to that of the amorphous powder coatings. Key Words:semi-crystal polyester resin; powder coating; anti-aging properties 聚酯粉末涂料主要由聚酯树脂、异氰脲酸三缩水 甘油酯(TGIC)固化剂、颜填料和助剂等组成其中聚 酯树脂对涂膜性能起关键作用。聚酯树脂按其聚集 态可分为无定形和半结晶型一般来说,无定形聚酯 树脂其显著特点是玻璃化温度与熔融黏度呈现出正 相关性即黏度越大破璃化温度越高。而对于粉末 涂料则期望聚酯树脂有较高的玻璃化温度保证贮存 稳定性又希望聚酯树脂具有较低的熔融黏度这样 粉末涂料固化时就更容易获得流平性能更好的涂层， 同时较低的熔融黏度又更容易实现低温固化。由于 传统无定形聚酯树脂无法同时满足较高的玻璃化温 度和较低的熔融黏度的要求因此人们借鉴了半结 晶型聚合物的理化特性，合成半结晶型聚酯树脂，有 效解决了无定形聚酯树脂无法同时满足较高的玻璃 化温度和较低熔融黏度的问题，从而获得性能更优异 的粉末涂料涂层[1。户外粉末涂料的耐候性能是决 定其使用寿命的关键因素，对于无定形聚酯粉末涂料 耐候性能的研究已有大量的报道12-31,而对于半结晶 型聚酯树脂粉末涂料的研究主要集中于应用方面，如 低温固化行为4、涂膜消光5)、改善流平性能6)等， 对其耐候性能的研究则报道较少。本研究通过合成 无定形和半结晶2类聚酯树脂，并制备粉末涂料，固 化成膜后通过人工加速老化试验机(QUV - B灯)试 验，考察了2 类聚酯粉末涂料涂层的耐候性能，并采 作者简介：李勇(1983一),男，工程师，主要从事粉末涂料用聚酯树脂、水性聚酯的合成研究。 工艺技术 工艺技术 用衰减全反射红外( ATR -FTIR)和扫描电镜(SEM) 研究粉末涂层老化降解规律为开发高性能聚酯粉末 涂料提供理论指导。 1 实验部分 1.1 实验原材料 新戊二醇(NPG):工业级吉林巴斯夫；16- 己 二醇(